mhec powder price-Effect of Methyl Hydroxyethyl Cellulose on the Performance of Foam Concrete
Following the addition of Methyl Hydroxyethyl Cellulose to 0.5% in foamed concrete, the slump decreased slightly. The data clarified that when the content of hMethyl Hydroxyethyl Cellulose does not exceed 0.05%, the participation of Methyl Hydroxyethyl Cellulose can significantly improve the fluidity and viscosity of the foam concrete slurry. After the Methyl Hydroxyethyl Cellulose is dissolved, a moist and flexible film is formed between the solid particles and the gas bubbles, which has an excellent smooth effect during the mixing process. It also makes the bubbles change without being easily disillusioned. The free and uniform “balls” in the slurry effectively improve the fluidity of the fresh slurry: But if the amount of Methyl Hydroxyethyl Cellulose exceeds 0.5%, the slurry will become too viscous and the fluidity will be greatly reduced. Therefore, 0.05% Methyl Hydroxyethyl Cellulose not only ensures the slump, but also stabilizes the bubbles, which is ideal for mixing.
The height of the test block lowered in the mold after forming characterizes the effect of Methyl Hydroxyethyl Cellulose on the volume stability of the foam concrete. It can be seen that the dosage of 0.05% of Methyl Hydroxyethyl Cellulose is the ideal dosage, and when the amount of Methyl Hydroxyethyl Cellulose is 0.05%, the height increase is reduced. The analysis believes that when the Methyl Hydroxyethyl Cellulose is appropriate, it can also reduce the volume of the hardened body while improving the fluidity of the slurry.
The slurry is constantly losing water during the hardening process. The internal foam is constantly disillusioned, and the hardening body shortens inevitably. This causes the volume of the hardening body to be unstable, and the addition of Methyl Hydroxyethyl Cellulose provides both for the hardening body It has excellent water retention effect, and can stabilize the internal foam of the hardened body through the characteristics of slurry hardening and Methyl Hydroxyethyl Cellulose film hardening, and then has an outstanding foam stabilizing effect, reducing the volume of the hardened body.